ASTM A is a special ductile cast iron grade. It has comparatively high tensile strength, and also high elongation, so its is a good cast iron material. UNS F, ASTM A, ferritic, pearlitic, crankshafts, gears, rollers, Carbon represents the total carbon in the listed composition. Cerium is an optional. Partially Pearlitic Ductile Iron contains pearlite which makes it more wear resistant and This specification is similar to ASTM A grade
|Published (Last):||12 April 2012|
|PDF File Size:||1.40 Mb|
|ePub File Size:||6.29 Mb|
|Price:||Free* [*Free Regsitration Required]|
Or if you don’t have an account with us yet, then click here to register. Carbon represents brade total carbon in the listed composition. Actually, there is no equivalent grade with ASTM Athis is because most of ductile iron grades will require the tensile strength lower as MPa, or require it higher as MPa, so this material grade becomes special.
Brinell Hardness without heat treatment.
The data grace been submitted. Our Dandong foundry could produce this material, and herein, we share its chemical composition, mechanical and physical properties. Ductile iron has great vibration damping and good corrosion resistance properties.
Converted from Brinell hardness.
We advise that you only use the original value or one of its raw conversions in your calculations to minimize rounding error.
Ductile Iron Machining Advantages. Because of the comparatively high tensile strength and elongation, this material grade has been used for producing many types of iron castings, so it is a favorite ductile iron material grade of American clients.
80-55-06 Ductile Iron As Cast
It has comparatively high tensile strength, and also high elongation, so its is a good cast iron material. ASTM A is commonly used for municipal castings. Click here to view all the property values for this datasheet as gradf were originally entered into MatWeb. Most ductile irons are specified based on mechanical properties and have loosely defined compositions. For more information on 80-555-06 iron, go to our ductile iron page.
Cerium is an optional constituent in ductile iron.
When considering a conversion from a fabrication to a casting, ductile iron should be used for the reasons listed above castability, machining, close to steel strengths, and costs. ASTM A is a special ductile cast iron 80-55–06. This is just an approximate chemical composition range, which can not be used to guide production.
Main Application of Ductile Iron ASTM A Because of the comparatively high tensile strength and elongation, this material grade has been used for producing many types of iron castings, 8-55-06 it is a favorite ductile iron material grade of American clients.
Ductile Iron grade
Applications include crankshafts, gears and rollers. To see MatWeb’s complete data sheet for this material including material property data, metal compositions, material suppliers, etcplease click the button below. It has mechanical properties comparable to low alloy steels. This is in part because the gross material being used is less for brade ductile iron than for steel.
Ductile Iron As Cast | Alro Steel
However, this range can not be taken as the standard of inspection, unless there is special requirement. Impact Properties Ductile Iron impact properties are microstructure dependent. Compressive Strength Ksi MPa. Data sheets for overmetals, plastics, ceramics, and composites. We appreciate your input. The contents, results, and technical data from this site may not be reproduced either electronically, photographically or substantively without permission from MatWeb, LLC.
Login to see your most recently viewed materials here. No numerical rating available. MatWeb is intended for personal, non-commercial use. Questions or comments about MatWeb? trade
Please contact us at webmaster matweb. The followings are some ductile iron parts axtm by our dandong foundry in China. Ductile iron is one grade in a family of many.